DAIKOFCW 430

FCAW
  • FERRITIC - MARTENSITIC STAINLESS STEEL
430

Description

Rutile cored wire for 430 martensitic stainless steels
This wire deposits a ferritic stainless steel with good ductility in heat treated condition. Application include welding of similar parental metal, weld overlay and thermal spraying. Welding with this filler metal usually requires preheating and post weld heat treatment. The easy handling and the high deposition rate result in high productivity, excellent welding performance and very low spatter formation. Optimum mechanical properties and corrosion resistance are obtained only when the weldment is heat treated following the welding operation.
Specifications
EN ISO 14700
T Fe 8
Shielding
M21
Positions
PA, PB, PC
Current
DC+
Packaging Type
BS300 spool

Pren

17.5

Hardness

220HB - 250HB
Chem. Comp. %
DEFAULT
C
0.11
Mn
0.15
Ni
0.1
Cr
17.5
Nb
0.75
P
0.01
S
0.02
Si
0.4
Mechanical Properties
min
variant
Tensile strength Rm MPa
-
540
Yield strength Rp0.2 MPa
-
390
Elongation A (L0=5d0) %
-
26
Impact Charpy ISO-V
-
-
Impact Charpy ISO-V
-
-
Welding Parameters
1.2 mm
1.6 mm
Ampere
120A - 290A
180A - 350A
Voltage
20V - 30V
30V - 34V
Packaging
Ø 1,2÷1,6mm
Ø 1,2÷1,6mm
Packaging Type
BS300 spool
BS300 spool
Anti-wear Characteristics
Adhesive wear
Abrasive wear
Impact
Corrosion
Heat
430
Description

Application

Ferritic stainless steel 430 stands out for its excellent ductility when subject to heat treatments. This material is used in the welding of similar base metals, welding overlays, and thermal spraying. It is predominantly used for overlays on sealing surfaces of valves for gas, water, and steam, creating wear-resistant stainless steel coatings. During welding, it is essential to perform preheating and post-weld heat treatment to achieve the best mechanical properties and corrosion resistance. The composition is expertly balanced to provide sufficient chromium content to ensure adequate corrosion resistance in common applications while maintaining optimal ductility under heat treatment conditions. Niobium and/or titanium-stabilized variants are available, specifically developed for the automotive industry and used in the manufacture of exhaust systems. In these cases, preheating and post-weld heat treatment are also required.

Alloy Type

Ferritic stainless steels.

Microstructure

Ferrite.

Materials

Surfacing can be performed on all weldable base materials, unalloyed and low-alloyed. Welding of corrosion resistant chromium steels as well as other similar-alloyed steels with C-contents up to 0.20% (repair welding).
  • EN W.Nr.: 1.4001 (X7Cr14), 1.4006 (X12Cr13), 1.4057 (X17CrNi16-2), 1.4000 (X6Cr13), 1.4002 (X6CrAl13), 1.4016 (X6Cr17), 1.4059 (X17CrNi16-2), 1.4509 (X2CrTiNb18), 1.4510 (X3CrTi17), 1.4511 (X3CrNb17), 1.4512 (X2CrTi12), 1.4520 (X2CrTi17), 1.4712 (X10CrSi6), 1.4713 (X10CrAlSi7), 1.4724 (X10CrAlSi13), 1.4742 (X10CrAlSi18)
  • ASTM: 403, 405, 409, 410, 429, 430, 430Cb, 430Ti, 439, 431, 442
  • UNS: S40300, S40500, S40900, S41000, S42900, S43000, S43035, S43036, S43100, S44200

Welding & PWHT

This ferritic stainless steel is superior in mechanical performance with adequate carburization resistance. It is extensively used in welding to obtain overlays resistant to thermal and mechanical stress. Preheating and postweld thermal treatment are recommended for optimal welding results.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto