DAIKOWM 430

GMAW
  • FERRITIC - MARTENSITIC STAINLESS STEEL
430

Description

Ferritic solid wire for 17%Cr stainless steels
This wire rod deposits a ferritic stainless steel with good ductility in heat treated condition. Application include welding of similar parental metal, weld overlay and thermal spraying. Welding with this filler metal usually requires preheating and post weld heat treatment. Optimum mechanical properties and corrosion resistance are obtained only when the weldment is heat treated following the welding operation.
Specifications
ISO 14343-A
G 17
AWS A5.9
ER430
Shielding
M12, M13
Positions
PA, PB, PC, PD, PE, PF, PG
Current
DC+
Packaging Type
Drums, B300, D200 and D100 spools.
Asme qualifications
F-No (QW432)
6
A-No (QW442)
7

Pren

19.475

Hardness

220HB - 250HB
Chem. Comp. %
DEFAULT
C
0.1
Mn
0.6
Ni
0.6
Cr
17
P
0.03
S
0.03
Mo
0.75
Si
0.5
Cu
0.75
Mechanical Properties
min
variant
Tensile strength Rm MPa
450
530
Yield strength Rp0.2 MPa
300
410
Elongation A (L0=5d0) %
15
25
Impact Charpy ISO-V
-
-
Impact Charpy ISO-V
-
-
Welding Parameters
1 mm
1.2 mm
Ampere
160A - 220A
200A - 270A
Voltage
25V - 29V
26V - 30V
Packaging
Ø 0,8÷1,6mm
Ø 0,8÷1,6mm
Packaging Type
Drums, B300, D200 and D100 spools.
Drums, B300, D200 and D100 spools.
Anti-wear Characteristics
Adhesive wear
Abrasive wear
Impact
Corrosion
Heat
430
Description

Application

This is a ferritic stainless steel exhibiting good ductility in the heat-treated condition. Applications include welding similar parent metal, weld overlay, and thermal spraying, with a primary use in surfacing sealing faces of gas, water, and steam valves to achieve stainless and wear-resistant overlays. Welding with this filler metal typically necessitates preheating, normally 150°C, and postweld heat treatment for optimal mechanical properties and corrosion resistance. The balanced composition ensures sufficient chromium for corrosion resistance in usual applications while retaining ample ductility in the heat-treated state. Additionally, there are stabilized versions with Niobium and/or Titanium designed for the automotive industry, particularly in exhaust system production, requiring similar preheating and postweld heat treatment.

Alloy Type

Ferritic stainless steels.

Microstructure

Ferrite.

Materials

Surfacing can be performed on all weldable base materials, unalloyed and low-alloyed. Welding of corrosion resistant chromium steels as well as other similar-alloyed steels with C-contents up to 0.20% (repair welding).
EN W.Nr.: 1.4001 (X7Cr14), 1.4006 (X12Cr13), 1.4057 (X17CrNi16-2), 1.4000 (X6Cr13), 1.4002 (X6CrAl13), 1.4016 (X6Cr17), 1.4059 (X17CrNi16-2), 1.4509 (X2CrTiNb18), 1.4510 (X3CrTi17), 1.4511 (X3CrNb17), 1.4512 (X2CrTi12), 1.4520 (X2CrTi17), 1.4712 (X10CrSi6), 1.4713 (X10CrAlSi7), 1.4724 (X10CrAlSi13), 1.4742 (X10CrAlSi18).
ASTM: 403, 405, 409, 410, 429, 430, 430Cb, 430Ti, 439, 431, 442.
UNS: S40300, S40500, S40900, S41000, S42900, S43000, S43035, S43036, S43100, S44200.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Contact us
Daiko supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto