DAIKOWT 430LNbTi

GTAW
  • FERRITIC - MARTENSITIC STAINLESS STEEL
430

Description

Ferritic rod stabilized with Nb-Ti for stainless steels with 17% Cr
Rod that deposits ferritic stainless steel stabilized with niobium and titanium, ensuring good ductility even after heat treatment. Niobium and titanium are essential to prevent intergranular corrosion phenomena and to improve high temperature resistance. Typical applications include welding of similar base metals, overlays in the automotive industry, and in the production of exhaust systems. Preheat and post-weld heat treatment are generally required.
Specifications
EN ISO 14343-A
(W 18LNb)
AWS A5.9
(ER430)
Shielding
I1
Positions
PA, PB, PC, PD, PE, PF
Current
DC-
Packaging Type
5kg carton tube
Asme qualifications
F-No (QW432)
6
A-No (QW442)
7

Pren

18

Hardness

220HB - 250HB
Chem. Comp. %
DEFAULT
C
0.03
Mn
0.55
Ni
0.2
Cr
18
P
0.02
S
0.02
Si
0.65
Mechanical Properties
min
variant
Tensile strength Rm MPa
410
420
Yield strength Rp0.2 MPa
220
275
Elongation A (L0=5d0) %
15
26
Impact Charpy ISO-V
-
-
Impact Charpy ISO-V
-
-
Welding Parameters
1.6 mm
2.4 mm
Ampere
80A - 100A
110A - 160A
Voltage
-
-
Packaging
Ø 1,0÷4,0mm
Ø 1,0÷4,0mm
Packaging Type
product.packaging_types.product.packaging_types.product.packaging_types.5 kg Kartonröhre
product.packaging_types.product.packaging_types.product.packaging_types.5 kg Kartonröhre
430
Description

Application

Ferritic stainless steel 430 stands out for its excellent ductility when subject to heat treatments. This material is used in the welding of similar base metals, welding overlays, and thermal spraying. It is predominantly used for overlays on sealing surfaces of valves for gas, water, and steam, creating wear-resistant stainless steel coatings. During welding, it is essential to perform preheating and post-weld heat treatment to achieve the best mechanical properties and corrosion resistance. The composition is expertly balanced to provide sufficient chromium content to ensure adequate corrosion resistance in common applications while maintaining optimal ductility under heat treatment conditions. Niobium and/or titanium-stabilized variants are available, specifically developed for the automotive industry and used in the manufacture of exhaust systems. In these cases, preheating and post-weld heat treatment are also required.

Alloy Type

Ferritic stainless steels.

Microstructure

Ferrite.

Materials

Surfacing can be performed on all weldable base materials, unalloyed and low-alloyed. Welding of corrosion resistant chromium steels as well as other similar-alloyed steels with C-contents up to 0.20% (repair welding).
  • EN W.Nr.: 1.4001 (X7Cr14), 1.4006 (X12Cr13), 1.4057 (X17CrNi16-2), 1.4000 (X6Cr13), 1.4002 (X6CrAl13), 1.4016 (X6Cr17), 1.4059 (X17CrNi16-2), 1.4509 (X2CrTiNb18), 1.4510 (X3CrTi17), 1.4511 (X3CrNb17), 1.4512 (X2CrTi12), 1.4520 (X2CrTi17), 1.4712 (X10CrSi6), 1.4713 (X10CrAlSi7), 1.4724 (X10CrAlSi13), 1.4742 (X10CrAlSi18)
  • ASTM: 403, 405, 409, 410, 429, 430, 430Cb, 430Ti, 439, 431, 442
  • UNS: S40300, S40500, S40900, S41000, S42900, S43000, S43035, S43036, S43100, S44200

Welding & PWHT

This ferritic stainless steel is superior in mechanical performance with adequate carburization resistance. It is extensively used in welding to obtain overlays resistant to thermal and mechanical stress. Preheating and postweld thermal treatment are recommended for optimal welding results.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto