DAIKOFCW 102S

FCAW
  • CARBON STEELS
STRUCTURAL STEEL

Description

All position rutile flux cored wire for welding C and CMn steels
Folded flux cored wire for single or multipass welding C and C-Mn steels up to a yield strength of 420 MPa. Suitable for Argon-CO2 as well as pure CO2 welding it ensures good mechanical properties till -20°C. The main features of this wire are excellent weldability in all positions, excellent bead appearance, low amount of spatters and easy to remove slag with no porosity issues even on primer plates and very good feeding performance are achievable.
Specifications
ISO 17632-A
T 42 2 P C1/M21 1 H5
AWS A5.20
E71T-1C/M
Certifications
CE, RINA
Shielding
M21, C1
Positions
PA, PB, PC, PD, PE, PF, PG
Current
DC+
Packaging Type
BS300, D200 spools
Asme qualifications
F-No (QW432)
6
A-No (QW442)
1
Chem. Comp. %
0
C
0.04
Mn
1.3
P
0.003
S
0.012
Si
0.68
Mechanical Properties
min
variant
Tensile strength Rm MPa
490
540
Yield strength Rp0.2 MPa
420
460
Elongation A (L0=5d0) %
20
25
Impact Charpy ISO-V
27J @ -20°C
47J @ -20°C
Impact Charpy ISO-V
-
-
Welding Parameters
0 mm
1 mm
Ampere
130A - 290A
170A - 400A
Voltage
18V - 30V
28V - 32V
Packaging
Ø 1,0÷1,6mm
Ø 1,0÷1,6mm
Packaging Type
BS300, D200 spools
BS300, D200 spools
Description

Application

Carbon-manganese (C-Mn) steels serve as the predominant structural steels extensively used across various applications in the engineering industry. Successful welding of C-Mn steel fabrications is generally achievable, provided the steel composition is known, necessary precautions are taken, and qualified procedures are adhered to. Weldability varies among C-Mn steels, with potential cracking mechanisms, including hydrogen cracking, solidification cracking, and reheat cracking, depending on specific circumstances. These consumables effectively resist such issues, emphasizing the importance of a meticulous welding procedure. While preheat and post-weld heat treatment (PWHT) may not be universally required, the actual specifications depend on the grade and thickness of the base material being welded. Attaining the required mechanical properties in a welded joint with C-Mn steels is achievable through the use of appropriate welding consumables. However, the intricate structural changes during the weld thermal cycle necessitate careful evaluation of properties such as heat-affected zone (HAZ) toughness and hardness.

Alloy Type

Consumables for welding mild and C-Mn steels of 340-510MPa tensile strength.

Microstructure

Predominantly ferrite.

Materials

Carbon and carbon-manganese steels encompass a wide range of structural and pressure-grade materials commonly used in construction, mechanical engineering, and industrial plant applications. Among the EN-standardized grades are non-alloy structural steels intended for general use, known for their good weldability and progressively higher mechanical strength. The “P” grades, on the other hand, are pressure vessel steels typically used in boilers and heat exchangers. Equivalent ASTM specifications cover a similar scope of applications and are widely adopted internationally for structural components, piping, and fittings exposed to pressure or high temperatures. Lastly, API specifications are typical of the oil & gas sector, particularly for the production of pipelines used in hydrocarbon transport, offering increasing levels of mechanical strength and specific performance requirements.
  • EN W.Nr.: S 235 JR, S 235 J0, S 235 J2+N, S 275, S 275 J0, S 275 J2+N, S 355 JR, S 355 J0, S 355 J2+N, S 355 K2+N, P 235 GH, P 265 GH, P 295 GH
  • ASTM: A36, A106 gr. A, A106 gr. B, A106 gr. C, A139, A210 gr. A1, A210 gr. C, A234 gr. WPB, A334 gr. 1, A216 gr. WCA, A216 gr. WCB, A216 gr. WCC
  • API: A, B, X42, X52, X60

DO YOU NEED HELP?

Go to our dedicated section or contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto