G-TECH CuSn7
SMAW
- COPPER ALLOYS
CuSn
Description
Electrode with special basic coating
It's particularly suitable for welding and recharging
of phosphorous bronze or similar, brass and for recharging cast iron and carbon steel.
It is used for the construction of pump blades, turbines, parts subject to wear, such as sliding guides, sliders, seats of
valves, for repairing foundry and plating defects on tough steel
to sea water. The higher tin content increases strength and wear resistance and increases the solidification temperature range during deposition of the weld metal (lower preheating to about 200°C is required).
Specifications
AWS A5.6
ECuSn-C
DIN 1733
CuSn7
Shielding
-
Positions
PA, PB, PC, PD, PF
Current
DC+
Packaging Type
Carton box
Asme qualifications
F-No (QW432)
33
A-No (QW442)
-
Hardness
90HB
Chem. Comp. %
DEFAULT
Mn
0.1
Sn
8
P
0.2
Mechanical Properties
min
variant
Tensile strength Rm MPa
280
340
Yield strength Rp0.2 MPa
-
140
Elongation A (L0=5d0) %
20
40
Impact Charpy ISO-V
-
-
Impact Charpy ISO-V
-
-
Welding Parameters
2.5
mm
3.2
mm
4
mm
Ampere
55A - 60A
80A - 90A
100A - 120A
Voltage
-
-
-
Packaging
pcs/kg
pcs/kg
pcs/kg
Packaging Type
Carton box
Carton box
Carton box