DAIKOWS 316L

SAW
  • AUSTENITIC STAINLESS STEELS
316L

Description

Solid wire for Mo bearing austenitic stainless steels
The presence of molybdenum provides creep resistance at elevated temperatures and pitting resistance in a halide atmosphere. This alloy has a low carbon content which makes it particularly recommended where there is a risk of intergranular corrosion. 316L is widely applied in the chemical and food processing industries as well as in ship building and various types of architectural structures. These consumables are used for Mo bearing austenitic stainless steels with 1.5 ÷ 3 Mo. 316 steels are used for their good resistance to pitting, many acids and general corrosion.
Specifications
EN ISO 14343-A
S 19 12 3 L
AWS A5.9
ER316L
Certifications
CE
Shielding
DAIKOFLUX 900-W
Positions
PA, PB, PC
Current
DC/AC
Packaging Type
K415 spool and drums.
Asme qualifications
F-No (QW432)
6
A-No (QW442)
8

Ferrite

2-10 FN

Pren

27.08

Hardness

200HV - 220HV
Chem. Comp. %
DEFAULT
C
0.015
Mn
1.4
Ni
12.8
Cr
18.5
P
0.015
S
0.01
Mo
2.6
Si
0.5
Cu
0.15
Mechanical Properties
min
variant
Tensile strength Rm MPa
510
570
Yield strength Rp0.2 MPa
320
435
Elongation A (L0=5d0) %
25
30
Impact Charpy ISO-V
-
40J @ -196°C
Impact Charpy ISO-V
-
-
Welding Parameters
2.4 mm
Ampere
300A - 400A
Voltage
27V - 33V
Packaging
Ø 2,0÷4,0mm
Packaging Type
K415 spool and drums.
Description

Application

These consumables are specifically designed for austenitic stainless steels containing molybdenum (Mo) at a concentration between 1.5% and 3%. They are also compatible with titanium (Ti) or niobium (Nb) stabilized variants, which include nitrogen within the same alloys. 316/316L type steels are highly valued for their excellent resistance to pitting, many acids, and general corrosion. However, the described 316L consumables are not suitable for use in structural applications at high temperatures with 316/316H steels. For cryogenic applications down to -196 °C, please refer to the specific 316LCF datasheet. No preheating is needed; the maximum interpass temperature is 250 °C, and post-weld heat treatment (PWHT) is not required.

Alloy Type

316L Mo bearing austenitic stainless.

Microstructure

Austenite with a controlled level of ferrite, normally in the range 2-10FN depending on the application.

Materials

  • EN W.Nr.: 1.4404 (X2CrNiMo 17-12-2), 1.4401 (x 5CrNiMo 17 12 2), 1.4436 (X 3 CrNiMo 17 13 3), 1.4406 (X 2 CrNiMoN 17 11 2), 1.4429 (X 2 CrNiMoN 17 13 3), 1.4408 (GX5CrNiMo19-11-2), 1.4437 (GX6CrNiMo18-12)
  • ASTM: 316L, 316, 316LN, CF3M, CF8M
  • UNS: S31603, S31600, S31653

Welding & PWHT

These consumables ensure optimal performance in welding operations by eliminating the need for preheating, while maintaining a strict interpass temperature control at a maximum of 250°C. The absence of a requisite post-weld heat treatment (PWHT) further simplifies the process and enhances efficiency, making them an indispensable choice for welding austenitic stainless steels in challenging environments.

DO YOU NEED HELP?

Go to our dedicated section or contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto