35.45

These alloys offer exceptional resistance to carburization and oxidation, surpassing alloys with a 25% Cr-35% Ni composition when used at temperatures up to 1150 °C. However, there is a slight decrease in creep resistance.
Main applications include use in pyrolysis coils and reformer tubes in the petrochemical industry. For significant thicknesses, preheating is recommended due to the material's low ductility. Generally, no post-weld heat treatment (PWHT) is required.

High carbon 35Cr-45Ni-1Nb to match heat-resisting castings, which are often micro-alloyed with Ti and Zr.

In the as-welded condition the multi-pass weld metal microstructure consists of austenite with primary eutectic and secondary precipitated carbides.

• PROPRIETARY: Paralloy H46M (Doncasters Paralloy), Manaurite® XT, XTM (Manoir Industries), Centralloy® ET45 Micro (Schmidt + Clemens), Lloyds T80, Lloyds T75MA (LBA), E3545Nb-MA (Engemasa)

Queste leghe richiedono un controllo preciso dei parametri di saldatura per garantire cuciture di qualità. L'utilizzo di materiali di apporto appropriati e il mantenimento di un ambiente di lavoro pulito possono influenzare significativamente l'integrità della saldatura. È cruciale monitorare le temperature interpass e l'apporto di calore per mitigare potenziali problemi legati alla fessurazione a caldo e alla stabilità della microstruttura. In casi specifici, l'impiego di velocità di raffreddamento controllate e lente può migliorare le proprietà meccaniche finali delle saldature, proteggendo da distorsioni indesiderate e tensioni residue.