DAIKOWT 2209

GTAW
  • DUPLEX - SUPERDUPLEX
2209

Description

Duplex stainless steel rod for welding 22% Cr ferritic-austenitic stainless steel
Rod for welding ferritic-austenitic duplex steels which, in addition to providing high tensile strength and toughness, offers excellent resistance to stress corrosion cracking and pitting. The service temperature ranges from -60 °C to 250 °C. Controlled dilution and careful purging are essential to obtain the best properties. It ensures high-quality standards and ease of use.
Specifications
EN ISO 14343-A
W 22 9 3 N L
AWS A5.9
ER2209
Certifications
CE, TUV
Shielding
I1
Positions
PA, PB, PC, PD, PE, PF
Current
DC-
Packaging Type
5kg carton tube
Asme qualifications
F-No (QW432)
6
A-No (QW442)
-

Ferrite

% 25-50

Pren

36.81
Chem. Comp. %
0
C
0.01
Mn
1.45
Ni
8.6
Cr
23.2
N
0.17
P
0.015
S
0.015
Mo
3.3
Si
0.45
Cu
0.05
Mechanical Properties
min
variant
Tensile strength Rm MPa
550
710
Yield strength Rp0.2 MPa
450
570
Elongation A (L0=5d0) %
20
36
Impact Charpy ISO-V
-
120J @ -50°C
Impact Charpy ISO-V
-
-
Welding Parameters
1.6 mm
2.4 mm
3.2 mm
Ampere
80A - 100A
110A - 160A
120A - 200A
Voltage
-
-
-
Packaging
Ø 1,0÷4,0mm
Ø 1,0÷4,0mm
Ø 1,0÷4,0mm
Packaging Type
5kg carton tube
5kg carton tube
5kg carton tube
2209
Description

Application

The 2209 subfamily is used in pipes, plates, fittings, and forgings made from duplex stainless steel. This type of steel has a microstructure composed of about 50% austenite with a ferritic matrix. This composition, together with the general level of alloying, ensures superior strength compared to conventional austenitic steels, such as type 316L. It also offers excellent corrosion resistance in a wide range of environments, along with notable resistance to chloride-induced stress corrosion cracking (CSCC) and pitting attack in chlorinated environments, such as seawater. These characteristics make the alloys particularly appreciated in offshore applications in the oil, gas, chemical, and petrochemical sectors, including piping systems, flow lines, risers, and manifolds.

Alloy Type

22%Cr standard ferritic-austenitic duplex stainless steels.

Microstructure

Multipass welds in the as-welded condition contain about 25–50% ferrite depending on dilution and heat input/cooling rate conditions.

Materials

  • EN W.Nr.: 1.4462 (X2CrNiMoN22-5-3), 1.4362 (X2CrNiN23-4)
  • ASTM: A182 Gr F51, A890 Gr 4A (cast)
  • UNS: S31803, S32205, S32101, S32304, S32001, J92205
  • PROPRIETARY: SAF2205, SAF 2304 (Sandvik), Uranus® 45N, 35N (Industeel), A903 (voestalpine), Cronifer 2205LCN (VDM), Maresist F51 (Schmidt + Clemens), SM22Cr (Nippon Steel Corporation), LDX 2101 (Outokumpu)

Welding & PWHT

Generally, preheating is not necessary for welding. It is advisable to maintain a maximum interpass temperature of 150 °C. The heat input should be between 1.0 and 2.5 kJ/mm, depending on the material thickness; however, some codes limit the value to a maximum of 1.75 or 2.0 kJ/mm. Although welds on duplex stainless steels are almost always left as-welded, solution treatment is generally required for major repairs on castings. Studies and experience have shown that a water quench treatment at 1120 °C for 3-6 hours, with or without a cooling step at 1060 °C before quenching, imparts excellent metallurgical properties.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto