DAIKOFCW 120B

FCAW
  • HIGH YIELD STRENGTH STEELS
120ksi

Description

Basic flux cored wire for flat and horizontal position
Seamless basic flux cored wire for welding of very high strength Nickel-Chromium-Molybdenum alloyed steels with Ar-CO2 shielding gas. It displays excellent weldability in flat and horizontal positions, smooth and bright bead, less spatter, easy to remove slag and very high mechanical properties at low temperatures. Ease of slag removal reduces post-welding cleaning operations to a minimum. It is designed for those applications requiring 120 Ksi minimum tensile strength and good charpy v-notch toughness, such as when welding HY-80, HY-100, Strenx® 900, S890QL, S960Q.
Specifications
ISO 18276-A
T 89 4 Mn2Ni1CrMo B M 4
AWS A5.36
E120T5
Shielding
M21
Positions
PA, PB, PC
Current
DC+
Packaging Type
BS300 spool
Asme qualifications
F-No (QW432)
6
A-No (QW442)
10
Chem. Comp. %
DEFAULT
C
0.06
Mn
1.4
Ni
2.2
Cr
0.4
P
0.02
S
0.02
Mo
0.4
Si
0.4
Cu
0.15
Mechanical Properties
min
variant
Tensile strength Rm MPa
940
990
Yield strength Rp0.2 MPa
890
890
Elongation A (L0=5d0) %
15
15
Impact Charpy ISO-V
47J @ -40°C
47J @ -50°C
Impact Charpy ISO-V
-
-
Welding Parameters
1.2 mm
1.6 mm
Ampere
160A - 280A
180A - 350A
Voltage
18V - 30V
30V - 34V
Packaging
Ø 1,2÷1,6mm
Ø 1,2÷1,6mm
Packaging Type
BS300 spool
BS300 spool
Description

Application

Designed for applications demanding a minimum tensile strength of 120 Ksi and excellent Charpy V-notch toughness, these consumables are suitable for diverse structural uses. From lifting machines to shipbuilding, railway sectors to crane fabrication, they find application in various high-strength scenarios. Preheat as per base material and thickness; generally, a 100°C minimum preheat is needed for materials requiring these high-strength consumables. Exercise caution with some HSLA steels, as interpass temperatures above 200°C may compromise strength and toughness. Post-weld heat treatment (PWHT) depends on the base material and application.

Alloy Type

Mn-Ni-Mo low alloy consumables for welding high strength steels with ultimate tensile strength up to 825 MPa (120 ksi).

Microstructure

The microstructure of all the consumables is predominantly ferrite; some will contain high proportions of acicular ferrite for optimum aswelded toughness

Materials

This material is used for a variety of high strength steels. HY-80, HY-90, HY- 100. S890 and higher strength grades, thermo mechanically treated fine grain steels.
EN W.Nr.: S890QL, S960Q.
ASTM: A 709 Gr. 100 Type B, E, F, H, Q, HPS 100W.
PROPRIETARY: Strenx® 900 (SSAB), Alform® 900 X-treme (voestalpine).

DO YOU NEED HELP?

Go to our dedicated section or contact us
Daiko supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto