Application
The CuMnAl alloy is mainly used for joining and surfacing on complex aluminum bronzes, particularly on materials with a high manganese content, as well as on steel and cast steel. Thanks to its excellent resistance to seawater and corrosion, it is particularly suitable for the shipbuilding industry, finding applications in objects such as propellers, pumps, and fittings. In industrial chemistry, it is ideal for components such as valves, guides, and pumps, especially when exposed to chemical attacks combined with erosion. Its good friction coefficient makes it perfect for overlays on wavy surfaces, sliding surfaces, bearings, and matrices of all kinds. The weld deposit offers excellent mechanical properties, being robust and crack-resistant. It is characterized by excellent workability in chip removal, corrosion resistance, and non-magnetic properties. Before welding, it is essential to clean the area to achieve a bright metallic finish. For large welds, preheating to about 150°C is recommended, keeping the absorbed heat to a minimum and ensuring that the interpass temperature does not exceed 150°C.
Alloy Type
Highest grade of the Al-Bronze-types.
Microstructure
Consists of primary α-phase grains in a matrix composed mainly of γ-phase grains and an intergranular phase layer containing both α and γ-phase particles.
Materials
This alloy is also used to join or repair high-strength bronzes of similar chemical composition and for high-strength repairs of cast iron.

Products of the line CuMnAl

Product name Process AWS specifications EN ISO specifications
G-TECH 403 SMAW
AWS A5.6
ECuMnNiAl
-
DAIKOWM CuMn13Al GMAW
AWS A5.7
ERCuMnNiAl
EN ISO 24373
S Cu 6338
DAIKOWT CuMn13Al GTAW
AWS A5.7
ERCuMnNiAl
EN ISO 24373
S Cu 6338

DO YOU NEED HELP?

Go to our dedicated section or contact us
DAIKO supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto