Gr. 1
Application
The alloy, characterized by a high percentage of carbides, offers exceptional wear resistance, although this results in reduced impact and corrosion resistance. Due to the increased hardness, there is a tendency to crack during cooling, which can be minimized by carefully controlling preheating, interpass temperature, and post-heating techniques. Even though cobalt-chromium deposits soften slightly at high temperatures, they are generally considered immune to tempering. The welding metal deposited by the ERCoCr-C electrodes and rods is ideal for components like mixers and rotors, where extreme abrasion and limited impacts occur. Additionally, it is also suitable for pump sleeves, rotary seal rings, wear pads, extrusion screws, and bearing sleeves. The inclusion of tungsten improves high-temperature hardness and matrix toughness, ensuring excellent resistance to solid particle and adhesive erosion wear. It maintains a hardness of 43–58 HRC at temperatures up to 760 °C. Preheating to 300 °C and beyond is generally recommended.
Alloy Type
Cobalt alloy for hardfacing with excellent corrosion and abrasion resistance with low impact.
Microstructure
Primary hypereutectic carbides (approximately 19%) are
found in in an austenitic type matrix.
Materials
It bonds well with all steels including stainless.
Welding & PWHT
Prior to welding, it is essential to meticulously clean the joint surface and adjacent area, removing grease, oil, markings, sulfur compounds, and other impurities. It is advisable to avoid contact with copper or copper-based materials in the joint area. While not mandatory, the alloy yields better results when welded in the solution annealed state. As a rule, preheating is not necessary, provided the base metal is above 0 °C. Interpass temperatures should be kept low. It is effective to delay post-welding to 600 °C and slow down cooling to prevent cracking.
Products of the line Gr. 1
Product name | Process | AWS specifications | EN ISO specifications | |
DAIKOFCW 1010 | FCAW |
AWS A5.21
ERCCoCr-C |
- | |
G-TECH 1010 | SMAW |
AWS A5.13
ECoCr-C |
- | |
DAIKOWT 1010 | GTAW |
AWS A5.21
ERCoCr-C |
- | |
DAIKOWM 1010 | GMAW |
AWS A5.21
ECoCr-C |
- |