G-TECH 99

SMAW
  • CAST IRON
Ni CI

Description

Pure nickel basic-graphite coated electrode for cast iron
Basic-graphite special coated electrode with a pure nickel core wire. Suitable for cold welding on grey cast iron, malleable cast iron, and cast steel as well as repair welding on castings showing symptoms of fatigue. Excellent welding properties also for welding with low amperage. Quietly and intensely flowing weld metal, only few spattering, easily removable slag. The weld seam is soft and machinable even in the transitional zone between the seam and the base material.
Specifications
ISO 1071
E C Ni-CI 1
AWS A5.15
ENi-CI
Shielding
-
Positions
PA, PB, PC, PD, PE, PF
Current
DC+
Packaging Type
Carton box

Hardness

170HB
Chem. Comp. %
DEFAULT
C
1
Mn
0.2
S
0.02
Si
0.7
Fe
3
Mechanical Properties
min
variant
Tensile strength Rm MPa
270
300
Yield strength Rp0.2 MPa
250
270
Elongation A (L0=5d0) %
6
8
Impact Charpy ISO-V
-
-
Impact Charpy ISO-V
-
-
Welding Parameters
2.5 mm
3.2 mm
4 mm
Ampere
70A - 90A
90A - 120A
120A - 140A
Voltage
-
-
-
Packaging
pcs/kg
pcs/kg
pcs/kg
Packaging Type
Carton box
Carton box
Carton box
Ni CI
Description

Application

Pure nickel consumables serve a vital role in the welding and repair processes involving standard grades of grey cast irons and malleable cast irons. These consumables yield low-strength deposits, providing a distinct advantage as they can be easily machined, even when applied in thin layers. The inherent resistance to hardening in diluted weld metal enhances their utility, particularly for buttering applications prior to the use of more economically efficient NiFe consumables. Beyond their primary applications, pure nickel consumables demonstrate versatility by facilitating the joining of these cast irons with other materials, including steels, monels, copper, etc. This proves especially beneficial in scenarios where high strength is not the foremost requirement. Typical components that benefit from the application of pure nickel consumables include a wide array of general engineering castings. These encompass crucial elements such as machine bases, engine blocks, gear housings, and similar structures that operate under relatively low stresses. The adaptability and effectiveness of pure nickel consumables make them integral to the fabrication and maintenance of components in various engineering applications.

Alloy Type

Pure nickel type for welding cast iron.

Microstructure

Austenitic nickel with finely distributed graphite.

Materials

Grey iron.
EN W.Nr.: 1561:2011 Grey cast irons+
ASTM: A159, A319, A126, A48.

Welding & PWHT

Welding is commonly performed without preheat, although scenarios involving heavy multipass deposits or highly restrained joints may necessitate preheat, potentially reaching up to 150°C. Before initiating the welding process, it is crucial to prepare surfaces meticulously, employing careful gouging and/or grinding with limited heat application to prevent the propagation of cracks. The designated welding area should be cleaned diligently, removing contaminants such as sand, oil, grease, paint, or rust to the greatest extent possible. Preheating proves advantageous for eliminating impregnated oil on used castings undergoing repairs. In instances where welding is conducted without preheat, it is advisable to minimize the width of the Heat-Affected Zone (HAZ) by utilizing a low heat input and maintaining a low interpass temperature. The application of a skip welding technique can be beneficial in achieving this objective. For welds involving thicker sections or highly restrained conditions, preheat up to 150°C may become imperative. Light peening, aimed at reducing contraction stresses, can offer additional benefits, though caution is warranted to prevent the depletion of weld metal ductility. Buttering the joint faces or the sides of the repair cavity before the filling process can be a desirable practice, whether or not preheat is applied. Upon completion of the welding process, it is recommended to allow the workpiece to cool gradually, with the option of using insulation if deemed necessary for optimal results.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Contact us
Daiko supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto