DAIKOWM Ti 12

Gr. 12 titanium.

Single-phase and near single-phase alpha alloys (compact hexagonal lattice-HCP).

Grad 12, Ti-0.3Mo-0.8Ni.

Titanium, being a reactive metal, is susceptible to embrittlement when exposed to elevated temperatures and certain contaminants, including oxygen, nitrogen, and hydrogen. To prevent such issues, it is imperative to shield the metal from atmospheric contamination, which is achieved by using welding-grade inert gas during the welding process. Throughout arc welding, the titanium should remain shielded from the ambient air atmosphere until it cools below approximately 430°C. For optimal welding results, the titanium metal must be devoid of thick oxide and chemically clean before initiating the welding process. Contamination from oxide, water, grease, or dirt can lead to embrittlement. Therefore, it is essential to ensure that titanium welding rods are not only chemically clean but also free of heavy oxide, absorbed moisture, grease, and dirt. In instances where the weld bead maintains its bright and silvery appearance, cleaning between passes is generally unnecessary. However, if straw or light blue discoloration is observed on the weld, it can be remedied by wire brushing using a clean stainless steel wire brush. Conversely, if the weld beads display signs of contamination, such as dark blue, gray, or white powdery discoloration, thorough removal through grinding is mandatory. Following the removal of contaminated weld beads, the joint should be meticulously prepared and cleaned before commencing with subsequent welding operations.