DAIKOWT 310Mn

GTAW
  • SUPERAUSTENITIC STEELS
310

Description

Rod for stainless steel with 25% Cr-20% Ni-3% Mn
Modified 310 rod for joining and overlay of similar and corresponding heat-resistant steels, rolled, forged, and cast, used in annealing and quenching plants, steam boiler construction, crude oil, and ceramics sectors. Manganese is added to the formulation to enhance hot working properties and to increase strength, toughness, and hardenability. Avoid the temperature range between 650 and 900 °C due to the risk of embrittlement.
Specifications
EN ISO 14343-A
W 25 20
AWS A5.9
(E310)
Shielding
I1
Positions
PA, PB, PC, PD, PE, PF
Current
DC-
Packaging Type
5kg carton tube
Asme qualifications
F-No (QW432)
6
A-No (QW442)
-

Pren

25.1

Hardness

85HRB
Chem. Comp. %
DEFAULT
C
0.12
Mn
3.3
Ni
20.4
Cr
25.1
P
0.01
S
0.005
Si
1
Mechanical Properties
min
variant
Tensile strength Rm MPa
550
610
Yield strength Rp0.2 MPa
350
400
Elongation A (L0=5d0) %
20
35
Impact Charpy ISO-V
-
90J @ 20°C
Impact Charpy ISO-V
-
32J @ -196°C
Welding Parameters
1.6 mm
2.4 mm
Ampere
80A - 100A
110A - 160A
Voltage
-
-
Packaging
Ø 1,0÷4,0 mm
Ø 1,0÷4,0 mm
Packaging Type
product.packaging_types.product.packaging_types.product.packaging_types.5kg carton tube
product.packaging_types.product.packaging_types.product.packaging_types.5kg carton tube
310
Description

Application

The product is primarily used for welding 25% Cr-20% Ni (310) alloys, which can be wrought or cast, and contain up to 0.25% carbon. To ensure maximum resistance to cracking and microfissures during solidification, the manganese content in the welding metal is increased to 2-5%. The high alloy content of type 310 provides excellent oxidation resistance up to maximum temperatures of about 1200 °C, making it ideal for heat shields, furnace components, and ducts. These consumables are also suitable for mixed welds and dissimilar joints, including those where PWHT application is necessary. However, it is important to consider that the relatively high thermal expansion coefficient may cause thermal fatigue in transition joints subjected to thermal cycling. In such situations, the use of nickel-based consumables is generally recommended. Further applications include cushioned layers and overlays. The fully austenitic welding metal is suitable for specialized applications requiring low magnetic permeability (typically <1.01). Additionally, 310 welding metals intrinsically withstand temperatures down to –196 °C, making them suitable for cryogenic installations. Preheating is not necessary. It is preferable to maintain the interpass temperature below 150 °C and heat input below 1.5 kJ/mm; this is crucial especially for processes with high heat input, such as SAW.

Alloy Type

25%Cr-20%Ni (310) stainless steel.

Microstructure

Fully austenitic.

Materials

  • EN W. N.: 1.4826 (GX40CrNiSi22-10), 1.4828 (X15CrNiSi2012,), 1.4837 (GX40CrNiSi25-12), 1.4840 (GX15CrNi2520), 1.4841 (X15CrNiSi25-21), 1.4846 (X 40 CrNi 25-21), 1.4847 (X 8 CrNiAlTi 20-20), 1.4848 GX40CrNiSi25-20), 1.4335 (X1CrNi25-21), 1.4435 (X2CrNiMo18-14-3), 1.4446 (X1CrNiMoN22-25-3), 1.4547 (X3CrNiMoTi25-25)
  • ASTM: 310, 310S, CK20, 305, 314, 725LN, 316L
  • UNS: S31000, S31008, S31050, S31603

DO YOU NEED HELP?

Go to our dedicated section or contact us
DAIKO supporting the environment
Group
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto