DAIKOWT 308LSi

GTAW
  • AUSTENITIC STAINLESS STEELS
308L

Description

Solid rod for 304L base materials with silicon
These consumables are used to weld 18/8 stainless steels. Mainly applications include food industries, pharmaceutical equipment and general fabrication. Typical service temperatures are -100°C to 400°C. The higher silicon content (if compared with standard 308L) increases the welding fluidity and improve the bead appearance. Higher silicon content also improves wetting of the weld metal and potentially higher travel speeds compared to standard 308L products.
Specifications
ISO 14343-A
W 19 9 L Si
AWS A5.9
ER308LSi
Certifications
CE
Shielding
I1
Positions
PA, PB, PC, PD, PE, PF
Current
DC-
Packaging Type
5kg carton tube
Asme qualifications
F-No (QW432)
6
A-No (QW442)
8

Ferrite

3-12 FN

Pren

20.33

Hardness

76HRB
Chem. Comp. %
DEFAULT
C
0.01
Mn
1.7
Ni
10
Cr
20
P
0.015
S
0.01
Mo
0.1
Si
0.8
Cu
0.15
Mechanical Properties
min
variant
Tensile strength Rm MPa
510
570
Yield strength Rp0.2 MPa
320
435
Elongation A (L0=5d0) %
25
40
Impact Charpy ISO-V
-
70J @ -196°C
Impact Charpy ISO-V
-
-
Welding Parameters
1.6 mm
2.4 mm
Ampere
80A - 100A
110A - 160A
Voltage
-
-
Packaging
Ø 1,0÷4,0 mm
Ø 1,0÷4,0 mm
Packaging Type
5kg carton tube
5kg carton tube
Description

Application

Engineered for welding 18Cr/8Ni stainless steels, encompassing 301, 302, 303, nitrogen-bearing 304LN, and titanium-stabilized 321, these welding consumables offer versatile performance. They perform well in service temperatures ranging from -100°C to about 400°C, making them suitable for applications in food, brewery, pharmaceutical equipment, architectural and general fabrication, as well as nuclear engineering. It's important to note that these consumables, specifically 308L, are not recommended for elevated temperature structural applications involving 304/304H; refer to 308H for such applications. For cryogenic use at -196°C, consult 308LCF. No preheating is required, and the recommended maximum interpass temperature is 250°C, with no post-weld heat treatment necessary.

Alloy Type

308L austenitic stainless steels for joining 304L base materials.

Microstructure

Austenite with a controlled level of ferrite, normally in the range 3-12FN depending on the application.

Materials


EN W.Nr.: 1.4306 (X2CrNi19-11), 1.4301 (X5CrNi18-10), 1.4311 (X2CrNiN18-10), 1.4308 (X5CrNi19-10), 1.4541 (X6CrNiTi18-10), 1.4543 (X 3 CrNiCuTi 12-9), 1.4561 (X1CrNiMoTi18-13-2), 1.4550 (X6CrNiNb18-10)+
ASTM: 304L, 304, 304LN, CF3, CF8, 321, 347.
UNS: S30403, S30400, S30453, S32100, S34700.

DO YOU NEED HELP?

Go to our dedicated section or contact us
Daiko supporting the environment
Questo sito si avvale di cookie necessari al suo funzionamento ed utili alle finalità illustrate nella cookie policy.

Carrello

Il carrello è vuoto