DAIKOWT 307Si

Applications for this subfamily include the welding of different materials such as mild steels, stainless steels, hardenable and ballistic steels, both among themselves and with other metals, with or without the need for preheating. The high manganese content ensures excellent dilution tolerance and resistance to hot cracking, unlike ballistic steels and type 309, which require a high ferrite content. In some situations, this material can effectively replace those with high nickel content in joints between cast iron and stainless steels. Welds subjected to post-weld heat treatment (PWHT) maintain good ductility and toughness down to -50°C. Additionally, it offers moderate resistance to scale formation at temperatures up to 850°C. It is ideal as a cushion layer for welding or repairing steels with 13% Mn used in crushing plants or earthmoving equipment. It is also recommended as an intermediate layer on cast iron before a hard facing. This consumable is designed for surfacing operations with hardening between 200 and 400 HV, and is well-suited for repairing alloy rails, sleepers, and crossings, avoiding preheating. However, the hardening rate is lower compared to steel with 13% Mn, and overlays beyond a single layer may collapse under heavy rolling loads.