DAIKOWM Mo.B

The alloy with a nominal 0.5% molybdenum offers a significant improvement in high-temperature performance compared to carbon-manganese steels (C-Mn). It is widely used in the
fabrication of vessels and
pipelines requiring resistance to creep rupture and ductility at temperatures up to about 450 °C. The molybdenum content also enhances resistance to hydrogen attack, making it ideal for use in chemical processing plants. The mechanical properties of the weld metal, both in the as-welded and stress-relieved conditions, are excellent for welding technical structural and general structural steels intended for ambient or sub-zero temperature service. Therefore, these consumables are closely related to high-strength manganese-molybdenum alloy steels. Preheat and interpass temperatures generally range from 100 °C to 250 °C, depending on the thickness of the material being welded and the degree of restraint. Post-weld heat treatment (PWHT) for tempering can vary depending on the applied code; extremes range from 550 °C to 720 °C, with the most common range being from 630 °C to 670 °C. For materials up to 20 mm thick, some codes allow omitting the PWHT.